Acid Type

Concentration

Exposure 1

Exposures 2-6

Hydrochloric

37%

Surface etched

No reaction

Nitric

70%

Surface etched

No reaction

Sulfuric

98%

Surface etched

No reaction

Phosphoric

85%

No reaction

No reaction

MOXIE 1600 CLEANER SEALER is a water based, non-toxic, non-flammable product composed of in-organic, chemically reactive, complex compounds allowing full penetration up to seven inches while removing deeply imbedded petroleum products. MOXIE 1600 CLEANER SEALER undergoes a chemical reaction with the by products of the curing process to form the highest density of cementitious materials, dramatically enhancing all of the natural characteristics of concrete and reducing the capillary voids to practically zero.

MOXIE 1600 CLEANER SEALER is available in the following packages:

Some hard troweled surface may need to be shot blasted first. Contact manufacturer, any free or loose dirt, grease, oil, efflorescence or foreign matter must be physically removed first.

MOXIE 1600 CLEANER SEALER is formulated solely for concrete and masonry products and should not be used on asphalt, metal, or wood products. Will not penetrate acrylic or non-porous rubber base paint. Should not be applied below 400F. MOXIE 1600 CLEANER SEALER will seal against hydrostatic pressure; however, flowing water must be stopped before application. Very damp, cold days may extend drying times. Higher temperature will shorten drying times.

Mist lightly with water prior to application. If acid washing make sure acid is COMPLETELY REMOVED AND NEUTRALIZED prior to application. Unless used as a curing agent it is recommended to wait 28 days before application. Surface will still be porous enough to insure proper absorption. Earlier application times are not deleterious and will result in higher compressive strengths. A clean surface is not required, however, heavily soiled surfaces should be cleaned to provide optimum results. Remove any wax, grease, rubber, acrylic based paint, or any other type of surface sealer. Sand blasting, scarifying, or bead/shotblasting may be required to allow MOXIE 1600 CLEANER SEALER to penetrate into the matrix of the concrete. Two coats are required above grade; three coats below grade. Application method depends on time/labor constraints. Method "One" is preferred.

1) Application Method One: Apply two coats of MOXIE 1600 CLEANER SEALER 24 hours apart. Apply first coat by saturating the surface. Broom out any puddling. On vertical surfaces allow approximately 12" rundown. When this is nearly dry, MIST WITH WATER to promote deeper penetration. After 24 hours, flood with water, allow to dry approx. 3 hours. REPEAT PROCESS FOR SECOND APPLICATION. If efflorescence (white crystalline salts) appear continued flooding is necessary every 24 hours until efflorescence no longer appears. Typically two to seven days. .

2) Application Method Two: Apply first coat by saturating the surface. Broom out any puddling. On vertical surfaces allow approximately 12" rundown. When this is nearly dry, apply second coat. Allow this to dry but not over 3 hours, then "mist" with water. After 24 hours, flood surface as in APPLICATION METHOD ONE.

NOTE: High porosity or below-grade applications may require a third coat. Apply third coat 48 hours after the second coat IN EITHER APPLICATION.

MOXIE 1600 CLEANER SEALER may be used as a curing compound, however, MOXIE 1500 Concrete Sealer is recommended. The best concrete cure can be obtained with one heavy application (approx. 250 to 300 sq. ft. per gallon) after initial set, prior to final finish. To moisture/vapor or alkali/efflorescence-proof proceed with APPLICATION METHOD TWO.